Pla polima REVODE105

Kukuru Apejuwe:

REVODE105 is one kind of modified PLA which is specifically designed for transparent straws. Properties of REVODE105   PLA resin REVODE105 Testing methods Physical properties Density (g/cm3) 1.25±0.05 GB/T1033-1986 Melt flow rate ( g/10min ,190℃/2.16Kg) 3-8 GB/T3682-2000 Heat distortion temperature (℃) 60   Molding shrinkage rate (parallel  melt flow direction) 0.005 ISO294-4:2001 Molding shrinkage (vertical melt flow direction) 0.003   ISO294-4:2001 Mechanical properties ...


  • Port: DALIAN/ XIINGANG/ NINGBO
  • Owo ofin: T/T
  • ọja Apejuwe

    ọja Tags

    REVODE105 jẹ ọkan irú ti títúnṣe Pla eyi ti o ti pataki apẹrẹ fun sihin ṣíṣẹ.

    -Ini ti REVODE105

      Pla resini REVODE105 igbeyewo awọn ọna
    ara-ini
    Iwuwo (g / cm3) 1.25 ± 0.05 GB / T1033-1986
    Yo sisan oṣuwọn (g / 10min, 190 ℃ / 2.16Kg) 3-8 GB / T3682-2000
    Ooru iparun otutu (℃) 60  
    Igbáti shrinkage oṣuwọn (afiwe yo sisan itọsọna) 0,005 ISO294-4: 2001
    Mọ shrinkage (inaro yo sisan itọsọna) 0,003   ISO294-4: 2001
    darí ini
    Agbara fifẹ (Mpa) 45-60 GB / T1040-2006
    Elongation ni Bireki (%) ≥ 10 GB / T1040-2006
    Ikolu agbara (KJ / m2, Izod) 3 GB / T1043-2008

    ohun elo:

    The Pla resini REVODE105 ni o dara fun processing ti ti kii ooru-sooro ati ki o sihin gbooro ṣíṣẹ, ko dara fun te ṣíṣẹ.

    processing Information

    Awọn REVODE105 resini le ti wa ni ilọsiwaju lori ibile polypropylene (PP) koriko extrusion igbáti ẹrọ. Nigba ti processing, jọwọ akiyesi:

    Mo ti: Awọn processing otutu (awọn kan pato otutu nilo lati wa ni iṣapeye):

    Ooru akọkọ apakan (sunmọ kikọ sii ọfun): 130-150 ℃, miiran ruju: 160-180 ℃ Pla resini REVODE105 bẹrẹ yo ni otutu loke 60 ℃, ni irú ti ga ju iwọn otutu ni ono ọfun nyorisi si resini agglomeration ati unsmooth ono, o ti wa ni niyanju lati tú itutu omi sinu jaketi ni ono ọfun apakan.

    Nitori REVODE105 jẹ diẹ brittle ju ibile PP resini, mejeeji pari le adehun nigbati gige paipu. O ti wa ni niyanju lati sakoso omi otutu ni omi ojò laarin 35 ati 40 ℃, rii daju paipu ni o ni ga otutu nigbati fun gige, bayi yago fun rorun wo inu.

    II: Awọ blending

    Ti o ba ti ọja rẹ nilo lati wa ni awọ, rii daju lati lo pataki awọ Yinki tabi Pla-orisun awọ titunto si ipele. Aibojumu Yinki tabi awọ titunto si ipele le ja si brittle ọja, unsmooth ọja dada ati paapa lagbara lati extrude.

    Ti o ba ti awọ blending ohun elo ko le ṣee lo soke laarin 2 wakati, o ti wa ni niyanju ko lo 25 kg / apo resini gbogbo ni ẹẹkan, dipo, lo idaji ti o ati ki o Igbẹhin awọn miiran idaji pẹlu kan gbona lilẹ ẹrọ ni ẹẹkan. Awọn idi ni lati fi awọn ohun elo ti si awọn air bi kuru bi o ti ṣee.

    III: gbigbe

    REVODE105 ti a ti ni ilọsiwaju nipasẹ gbigbe crystallization, ati awọn ọrinrin akoonu jẹ kere than400 ppm. Awọn resini ti o ti fipamọ ni Aluminiomu bankanje apo, ni idaabobo nipasẹ apoti tabi apo ita le ṣee lo taara. Pa awọn package kü titi setan lati lo ki o si kiakia reseal eyikeyi ajeku ohun elo, tabi awọn resini yoo fa ọrinrin. Lẹhin ju, awọn resini le mú ẹya pọ si arinbo nigba ti ilana, ati awọn ọja le ni brittle ini, dada shrinkage. Ti o ba ti resini fara ninu awọn bugbamu fun diẹ ẹ sii ju wakati kan, o yẹ ki o wa ni tun-si dahùn o ṣaaju ki o to lilo, bibẹkọ ti, awọn resini le ṣee lo taara. Awọn seese ti absorbing awọn ọrinrin ko le wa ni rara, ti o ba ti resini fara ninu awọn bugbamu pẹlu ga ọrinrin.

    Nigba ti tun-gbigbe awọn resini, awọn un-dehumidified gbona air wa ni ewọ, fun lai dehumidifier, ko nikan ni gbigbe ipa ko le wa ni gba, sugbon o tun awọn iyara ti omi absorbance ti Pla resini le ti wa ni onikiakia. Awọn dehumidified air le ẹri awọn gbigbe ipa ti Pla resini ni desiccator. Nigba lilo gbogbo lọla, awọn dehumidification ẹrọ yẹ ki o wa ni lo lati dehumidify afẹfẹ ninu oven.SD-H jara ti oyin-kẹkẹ-Iru dehumidifiers pese nipa Shini Pla stics Technologies Inc. ti wa ni strongly iṣeduro fun Pla gbigbe, miiran awọn ẹrọ pẹlu kanna dehumidified ipa le tun ti wa ti a ti yan.

    Aṣoju gbigbe awọn ipo ti wa ni han ninu tabili ni isalẹ:

    gbigbe paramita aṣoju Eto
    Ibugbe Time (wakati) 2-3
    Air otutu (℃) 80 (otutu ti deede lọla)
    Air ìri Point (℃) -40 (otutu ti dehumidifier)
    Air Flow Rate (M3 / hr-kg resini) > 1.85

    akiyesi:

    Pa awọn baffle ni isalẹ ti awọn hopper ki o si mú awọn agba nigba ti shutting isalẹ awọn ẹrọ fun igba diẹ (laarin 30 min), etanje ìdènà ti awọn kikọ sii ọfun. Ṣii awọn baffle ki o si ifunni resini lẹhin ifẹsẹmulẹ lati tun-bẹrẹ abẹrẹ.

    Ti o ba ti awọ iyipada ati decomposing sele nigba mọ ilana, mú awọn agba lẹsẹkẹsẹ lati mo daju ni ipinle ti awọn ohun elo. Pa lori nṣiṣẹ ti o ba ti awọn ohun elo ti ni deede, tabi ṣatunṣe sile.

    Imularada itoju ti sọdọtun ohun elo:

    Awọn jẹrisi awọn ọja produced ni awọn revode105 gbóògì ilana le ti wa ni ilọsiwaju ati ni ilọsiwaju pẹlu awọn titun materials.The o yẹ ti afikun yẹ ki o wa ju tobi, bibẹkọ ti awọn ọja yoo si wa ju brittle.

    Awọn tunlo ohun elo le ṣee ṣe mu ninu awọn wọnyi ọna meji:

    Ni awọn ilana ti gbóògì, o jẹ taara comminuted ati ki o mu si hopper nipa ọna ti laifọwọyi feeding.The titun awọn ohun elo ti wa ni adalu lilo, sugbon nilo lati rii daju wipe awọn garawa otutu ni ko ga ju 60 iwọn, bibẹkọ ti nibẹ ni o le jẹ alalepo ohun elo ( niyanju mode ti lilo)